Olugbade Temitope Olumide; Omiyale Babatunde Olamide: Corrosion resistance of surface-conditioned 301 and 304 stainless steels by salt spray test. In: Analecta technica Szegedinensia, (15) 2. pp. 9-19. (2021)
Előnézet |
Cikk, tanulmány, mű
engineering_2021_002_009-019.pdf Letöltés (287kB) | Előnézet |
Absztrakt (kivonat)
The corrosion rate of surface-conditioned 301 and 304 stainless steels (SS) was determined by salt spray test in a controlled accelerated corrosive medium (9.5 L of pure distilled water + 500 g NaCl). Surface conditioning via mechanical attrition treatment was firstly carried out before the salt spray test. The corrosion rate was determined by weight loss method before and after the salt spray test. Compared to the untreated 301 SS sample with a weight loss of 0.15 g, the surface-conditioned 301 SS samples treated for 300 s and 1200 s experienced a lower weight loss of 0.04 and 0.02 g, respectively. A similar reduction in weight loss was achieved for 304 SS sample when treated for 300, 600, and 1200 s.
| Mű típusa: | Cikk, tanulmány, mű |
|---|---|
| Befoglaló folyóirat/kiadvány címe: | Analecta technica Szegedinensia |
| Dátum: | 2021 |
| Kötet: | 15 |
| Szám: | 2 |
| ISSN: | 2064-7964 |
| Oldalak: | pp. 9-19 |
| Nyelv: | angol |
| Befoglaló mű URL: | http://acta.bibl.u-szeged.hu/74101/ |
| DOI: | 10.14232/analecta.2021.2.9-19 |
| Kulcsszavak: | Korrózió, Acél |
| Megjegyzések: | Bibliogr.: p. 17-19. ; ill. ; összefoglalás angol nyelven |
| Szakterület: | 01. Természettudományok 01. Természettudományok > 01.04. Kémiai tudományok |
| Feltöltés dátuma: | 2022. jan. 03. 09:56 |
| Utolsó módosítás: | 2023. júl. 13. 10:40 |
| URI: | http://acta.bibl.u-szeged.hu/id/eprint/74110 |
 |
Tétel nézet |