Production of refractory material of baddeleyite and corundum

Abdel Rehim A. M.: Production of refractory material of baddeleyite and corundum. In: Acta mineralogica-petrographica, (22) 2. pp. 353-361. (1976)

Előnézet

Cikk, tanulmány, mű mineralogica_022_fasc_002_353-361.pdf Letöltés (750kB) | Előnézet

Absztrakt (kivonat)

This work represents a study of the production of refractory material of baddeleyite and corundum from Rosetta zircon. This method is based on sintering of zircon with aluminum fluoride in presence of graphité. The desilication of zircon with the formation of baddeleyite and corundum was found to take place optimally at 850 °C at 1 hour using zircon, aluminium fluoride and graphite mixes of ratio 1:0.8 :0.1. Also, the behaviour of zircon was studied under different sintering conditions.

Mű típusa:	Cikk, tanulmány, mű
Befoglaló folyóirat/kiadvány címe:	Acta mineralogica-petrographica
Dátum:	1976
Kötet:	22
Szám:	2
ISSN:	0365-8066
Oldalak:	pp. 353-361
Nyelv:	angol
Kiadó:	University of Szeged, Department of Mineralogy, Geochemistry and Petrology
Kiadás helye:	Szeged
Befoglaló mű URL:	http://acta.bibl.u-szeged.hu/39395/
Kulcsszavak:	Kőzettan, Ásványtan, Földtan
Megjegyzések:	Bibliogr.: 361. p. ; összefoglalás angol nyelven
Szakterület:	01. Természettudományok 01. Természettudományok > 01.05. Föld- és kapcsolódó környezettudományok
Feltöltés dátuma:	2016. okt. 17. 09:25
Utolsó módosítás:	2022. júl. 22. 15:59
URI:	http://acta.bibl.u-szeged.hu/id/eprint/24610

Bővebben:

Tétel nézet